Posted: Sat Mar 03, 2012 3:50 pm Post subject: |
|
|
Jim Cooley wrote: | I haven't tried to "season" it per se, but it's already built up a nice finish which inhibits sticking. |
Well then, you're done. Move on, time for other things. Such as, enjoying some food cooked in your fancy pan.
xo, Biggles |
|
Back to top |
|
|
Dilbert
Joined: 19 Oct 2007 Posts: 1304 Location: central PA
|
Posted: Sat Mar 03, 2012 4:37 pm Post subject: |
|
|
after blasting that old Griswold I took the 'use it and it will happen' approach - although I did 'restrict' it to fatty stuff like bacon and high fat ground beef for a couple weeks. since I didn't need to have it seasoned to perfection by tonight's dinner time, it worked. it'll do fried eggs no problem - and the pan is light enough that I can toss & pan flip them for over easy. |
|
Back to top |
|
|
dindin
Joined: 18 Dec 2014 Posts: 1
|
Posted: Thu Dec 18, 2014 3:50 pm Post subject: seasoning carbon steel with flaxseed oil failure |
|
|
I tried the seasoning method here:
https://www.youtube.com/watch?v=xoIO8YOpyN4
Repeated this 12-14 times, it created a beautiful slick shiny black layer, just like in the video.
When I tried frying some hamburgers they stuck and when cleaning the pan seasoning came off partially. Hamburgers don't stick in my (seasoned by use) relatively new Lodge cast iron pan. I was expecting an even better result after seasoning this carbon steel pan this way.
So I must have done something wrong.
I used filtered flaxseed oil, made sure the oil was way past the smoking point each time, fully dried.
I can only think of 2 things that may have caused my problems.
1. Most people seem to recommend a temp of 500F for seasoning. I kept measuring temperature and I did go up to over 600F on the stovetop, and I kept the pan on there for a few minutes, until it stopped smoking completely. Now I'm not sure if I was partially burning off layers at 600-650F.
I know I can use the oven to maintain a steadier temp, but that is a much longer process.
So my questions are:
1) Should I make sure to stay around 500F on the stovetop, and not exceed 600F? Would that make a difference?
2) Is it necessary for the pan to cool down completely between cycles? Sometimes I let it come down to just below 200F before seasoning again. |
|
Back to top |
|
|
Dilbert
Joined: 19 Oct 2007 Posts: 1304 Location: central PA
|
Posted: Thu Dec 18, 2014 6:45 pm Post subject: |
|
|
if the "coating" flaked off, that's a pretty big indication the applied oil was too thick.
you can see in the video - perhaps a tablespoon of oil? wiped around with a paper towel, which likely absorbed 90% or more of the volume.
thin" is the operative word
many layers/repeats - eleven is mentioned.
overheated? that's possible. and overheating thick layers will make the situation worse.
as for cooling down, watch the video. he puts his hand flat on the bottom of the pan. despite asbestos chef fingers, that's not going to work at 200'F +/-
and this is why I use the "just cook fatty stuff until it is non-stick" method.....
I also have to point out the "if you need to reason" issue. I have pans that were "seasoned" in the 1940's. they don't need re-seasoning. the need to re-season is due to some goof in use / care. like when your Thanksgiving guest sister-in-law cleans it up with a Brillo pad . . . |
|
Back to top |
|
|
|
|
Cooking For Engineers Forum Index
-> Tools, Equipment, and Gadgets |
All times are GMT Goto page Previous 1, 2, 3, 4, 5, 6, 7, 8, 9, 10
|
Page 10 of 10 |
|
|
You can post new topics in this forum You can reply to topics in this forum You cannot edit your posts in this forum You cannot delete your posts in this forum You cannot vote in polls in this forum
|
Powered by phpBB © 2001, 2005 phpBB Group
|